LNP™ THERMOCOMP™ 2F004 compound
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BqSFMK_LNP-THERMOCOMP-2F004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP FP-EF-1004 is a fluoropolymer compound based on ETFE resin containing 20% Glass Fiber. Also known as: LNP* THERMOCOMP* Compound FP-EF-1004 Product reorder name: 2F004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.85 | g/cm³ | |
| -- | 1.84 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4870 | MPa | ASTM D638 |
| -- | 4410 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/5 |
| Break 3 | 49.0 | MPa | ASTM D638 |
| Break | 51.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 9.4 | % | ASTM D638 |
| Yield | 9.1 | % | ISO 527-2/5 |
| Break 5 | 11 | % | ASTM D638 |
| Break | 9.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 4020 | MPa | ASTM D790 |
| -- 7 | 3780 | MPa | ISO 178 |
| Flexural Stress | 72.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D256 |
| 23°C 8 | 45 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 97 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 21.0 | J | ASTM D3763 |
| -- | 10.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 240 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 219 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 112 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 300 to 325 | °C | |
| Front Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 0.170 to 0.340 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-765 | CHI MEI CORPORATION | ABS | POLYLAC® |
| CERTENE™ LLI-5026G | Muehlstein | LLDPE | CERTENE™ |
| InnoTuf® TP-4054 | Innovative Polymers, Inc. | TSU | InnoTuf® |
| Karina YELLOW PVC COMPOUND 550D02/101-AT-IS (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TRC 787N E C12616 | LyondellBasell Industries | PP Copolymer | Hostacom |