Kingfa PBT JE2-R2G20
| Category: | ABS+PBT , Acrylonitrile Butadiene Styrene + PBT |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BnYn2z_Kingfa-PBT-JE2-R2G20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT JE2-R2G20 is an acrylonitrile butadiene styrene PBT (ABS PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT JE2-R2G20 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 0.30 - 0.40 | % | ASTM D955 |
| Transverse flow : 23°C | 0.60 - 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 82 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3 | 7800 | MPa | ASTM D790 |
| Flexural Strength 4 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.30 mm | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 245 - 265 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 235 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 60.0 - 110 | °C | |
| Back Pressure | 0.300 - 1.00 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 265°CInjection Speed: 60 to 80% |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEDUR® L 9401-1 | ALBIS PLASTIC GmbH | PPS | TEDUR® |
| Bergamid™ A70 G30 U-S0 BK709 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Flontech® FT-PI15-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Durethan® BKV 50 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| TECHNYL eXten® D 218CR V33 BLACK | Solvay Engineering Plastics | Nylon 66/610 | TECHNYL eXten® |