Ravago Compounds PP-6444

Category:	PP Homopolymer , Polypropylene Homopolymer
Manufacturer:	Ravago Manufacturing Americas, LLC
Trademark:	Ravago Compounds
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BnUvq0_Ravago-Compounds-PP-6444.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Key Features:

Polypropylene Homopolymer

40% Talc filled

General Purpose

Designed for Injection molded applications

Good balance of processability and physical properties

General Information
Filler / Reinforcement	Talc filler, 40% filler by weight
Features	Homopolymer Workability, good General
Uses	General
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.25	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	22	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus - Tangent (23°C)	4370	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C)	21	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load			ASTM D648
0.45 MPa, not annealed	139	°C	ASTM D648
1.8 MPa, not annealed	90.0	°C	ASTM D648

Injection	Nominal Value	Unit
Drying Temperature	71.1 - 93.3	°C
Drying Time	0.0 - 8.0	hr
Rear Temperature	193 - 238	°C
Middle Temperature	193 - 238	°C
Front Temperature	193 - 238	°C
Nozzle Temperature	193 - 238	°C
Mold Temperature	26.7 - 60.0	°C
Back Pressure	0.00 - 0.689	MPa
Screw Speed	50 - 150	rpm

Injection instructions
Hot Runner Temperature (if applicable): 420 to 450°F

Resin Grade	Manufacturer	Category	Trademark
Starex SF-0950S	SAMSUNG SDI CO., LTD.	MABS	Starex
VITAMIDE® AY15BK6692	Jackdaw Polymers	Nylon 66	VITAMIDE®
HOPELEX PCN-2001TA	Lotte Chemical Corporation	PC	HOPELEX
KRATON® D1118 E	Kraton Polymers LLC	SBC	KRATON®
LNP™ THERMOCOMP™ AF004XXY compound	SABIC Innovative Plastics	ABS	LNP™ THERMOCOMP™