NYCOA Polyamide 2011
| Category: | Nylon+TPE , Polyamide + TPE |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bm1Eo8_NYCOA-Polyamide-2011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 2011 is a flexible Nylon copolymer TPE particularly suitable for extrusion applications. It has a moderately high melt viscosity, excellent processability and yields extremely tough and resilient finished articles. NYCOA 2011 is recommended for applications that demand easy flow, exceptional toughness, and flexibility with low moisture absorption. The high thermal and chemical resistance, inherent to Nylon 6, is retained. NYCOA 2011 is available with custom additive packages: heat stabilizer, UV stabilizer, flame retardant and/or customer colors. Typical applications include flexible tubing and fishing line. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.3 | % | ASTM D570 |
| Saturation | 6.5 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 57.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Flexural Modulus 3 | 469 | MPa | ASTM D790 |
| Flexural Strength 4 | 22.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 190 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 205 | °C |
| Additional Information |
|---|
| Water Extractable, NYCOA Method: 8 to 10 %The value listed as Melting Point was tested in accordance with ASTM D789.Tensile Elongation at Break, ASTM D638: 500+% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 238 | °C | |
| Front Temperature | 232 - 249 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 243 - 254 | °C | |
| Mold Temperature | 21.1 - 48.9 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 18.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SumiDurez PM 9750 | SumiDurez Singapore Pte Ltd | Phenolic | SumiDurez |
| Chemlon® MDF4 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Fainplast PVC GS 75/O | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Lucky Enpla LAY100F | Lucky Enpla Co LTD | PC+ABS | Lucky Enpla |
| Plaslube® PC-50/TF/13/SI/2 BK3585 | Techmer Engineered Solutions | PC | Plaslube® |