LNP™ STAT-KON™ MD000APH compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bm0DUE_LNP-STAT-KON-MD000APH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-KON* MD000APH is a compound based on Polypropylene resin containing Carbon Powder. Added features of this grade include: Electrically Conductive, Healthcare. Also known as: LNP* STAT-KON* Compound MD000APH Product reorder name: MD000APH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1530 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 1150 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 29.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 580 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 51.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 572E3720008, Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| mPact™ D139 | Chevron Phillips Chemical Company LLC | mLLDPE | mPact™ |
| Borealis PP HC600TF | Borealis AG | PP Homopolymer | Borealis PP |
| Formolene® HB5502S1 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Formolon® 622S | Formosa Plastics Corporation, U.S.A. | PVC, Rigid | Formolon® |