Cereplast Compostables® 6015
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlzRKX_Cereplast-Compostables-6015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 6015, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 6015 has been designed to have an excellent balance of strength, toughness and processability. Compostable 6015 can be processed on existing sheet extrusion machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. Compostable 6015 is recommended for extrusion applications like gift cards, sheet, printed displays and other sheet applications.… |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 58.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4170 | MPa | ASTM D790 |
| Flexural Strength | 80.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 45.0 | °C | ASTM D648 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 154 - 174 | °C | |
| Cylinder Zone 2 Temp. | 163 - 171 | °C | |
| Cylinder Zone 3 Temp. | 166 - 174 | °C | |
| Adapter Temperature | 166 - 174 | °C | |
| Melt Temperature | 199 | °C | |
| Die Temperature | 166 - 174 | °C |
| Extrusion instructions |
|---|
| Screw Speed: 20 to100 rpmDrying Temperature (regrind): 100 to120°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1032 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| Next Nylon 66 Prime Series PXF-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ALTECH® PP-H A 2030/159 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| KOPA® KN3311BLK | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Thermec S™ 4150RC65 | Technical Polymers, LLC | PPS | Thermec S™ |