Staramide AS3
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BlsKAz_Staramide-AS3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide AS3 is 15 % Glass Bead Reinforced Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.2 to 1.6 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3700 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 75.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 3200 | MPa | ISO 178 |
| Flexural Stress | 125 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4(23°C) | 20 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 5(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 20 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 230 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 85.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 240 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 5.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4790 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| ACCUTECH™ HP0339G20CL | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Kpren CM435 | Shandong Xuye New Materials Co., Ltd. | CM | Kpren |
| MAJORIS EX960 | AD majoris | PP, Unspecified | MAJORIS |
| ICORENE® 3940 | ICO Polymers NA, A Division of A. Schulman | LLDPE | ICORENE® |