DOW™ LDPE PG 7008 (Extrusion Coating)
| Category: | LDPE , Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BkVkL5_DOW-LDPE-PG-7008-Extrusion-Coating-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Dow LDPE PG 7008 Polyethylene Resin is typicalled used in extrusion coating applications. Dow LDPE PG 7008 Polyethylene Resin can be readily processed using conventional LDPE extrusion coating hardware of melt temperatures of 270 to 335°C, preferably less than 290°C, for best sensory performance. Dow LDPE PG 7008 Polyethylene Resin provides low volatile organic carbon (VOC) emissions in extrusion, contributing to low factory emissions and optimal sensory performance. When processed on suitable hardware, Dow LDPE PG 7008 Polyethylene Resin exhibits excellent draw down good edge stability and low neck-in. Applications:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 2% Secant | 160 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 8.00 | MPa | |
| Break | 10.0 | MPa | |
| Tensile Elongation (Break) | 450 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature 1 | 105 | °C | Internal Method |
| Water Vapor Transmission 2 | 270 | g/m²/24 hr | ASTM E398-83 |
| Minimum Heat Seal Temperature | 100 to 120 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Minimum Coating Weight 3 | 5.0 | g/m² | Internal Method |
| Neck-in 4 | 65.0 | mm | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Melting Temperature | 106 | °C | DSC |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 270 to 335 | °C |
| Note Message | |
|---|---|
| 1 . | Temperature required to reach 3 N/15 mm for a 25 g/m2 coating of PG 7008 onto paper |
| 2 . | 38°C, 90% RHDivide by coating weight in g/m² to obtain actual WVTR. |
| 3 . | 290°C set temperature. |
| 4 . | 100 m/min, 25 g/m² coatings at 290°C set temperature. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALLOY® B1800 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | PRIMALLOY® |
| SCANAMID 6 B11^ F50 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Andur 9000 AS | Anderson Development Company | PUR-TDI | Andur |
| Sylvin 83007-67 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 4200-85 Grey 9579 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |