Borlink™ LE4253DC
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BkErUv_Borlink-LE4253DC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Borlink LE4253DC is a crosslinkable natural polyethylene compound based on Supercure technology, specially designed for insulation of energy cables. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (Base Resin) | 0.922 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Moisture | < 200 | ppm | Karl Fisher |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Set 1 | IEC 60811-507 | ||
| Elongation under load : 200°C | < 180 | % | |
| Permanent deformation : 200°C | < 15 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gottfert Elastograph | < 0.65 | N·m | ISO 6502 |
| Methanol Wash | < 800 | ppm | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 17.0 | MPa | ISO 527-2/500 |
| Tensile Strain (Break) | > 450 | % | ISO 527-2/500 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strain at Break in Air (135°C, 168 hr) | < 20 | % | IEC 60811-401 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength 2 | > 22 | kV/mm | IEC 60243-1 |
| Dielectric Constant (50 Hz) | < 2.30 | IEC 60250 | |
| Dissipation Factor (50 Hz) | < 3.0E-4 | IEC 60250 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 125 to 135 | °C |
| Note Message | |
|---|---|
| 1 . | 0.20 MPa |
| 2 . | 50 Hz |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B11^FC | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Celstran® PA66-GF50-02 P11 | Celanese Corporation | Nylon 66 | Celstran® |
| DENKA POVAL K-17U6 | Denka Company Limited | PVOH | DENKA POVAL |
| Elastron® V V201.D51.N | Elastron USA, Inc. | TPV | Elastron® V |
| TechnoElast A 7000 I 1 nat | TechnoCompound GmbH | TPE | TechnoElast |