SABIC® PPcompound 8710U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bi9vBH_SABIC-PPcompound-8710U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8710U is a development grade, it is an elastomer-modified mineral filled Polypropylene for esthetic automotive exterior applications. This material has been designed to combine a good performance profile with good processing and excellent scratch performance. SABIC® PPcompound 8710U is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield, Injection Molded | 19.0 | MPa | |
| Break, Injection Molded | 14.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | 30 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1(Injection Molded) | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 4.0 | kJ/m² | |
| 0°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 115 | °C | ISO 75-2/B |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.5E-5 | cm/cm/°C | |
| 23 to 80°C | 7.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic PVDF 60100000 | 3M Advanced Materials Division | PVDF | 3M™ Dyneon™ Fluoroplastic |
| Avalon 50 | Greene, Tweed & Co. | PTFE | Avalon |
| EMLON® 6 GBR 20 FR V0 | EMAS Plastik San.Tic.AS. | Nylon 6 | EMLON® |
| Hifax EPR 60/M BIANCO | LyondellBasell Industries | PP Copolymer | Hifax |
| Lucolit® 1321 | Lucobit AG | TPO (POE) | Lucolit® |