Retpol® 400 TF HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bhf7YU_Retpol-400-TF-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Corton 400 TF HS is a 40% talc filled homopolymer polypropylene compound. It is a medium flow injection moulding grade developed for rigid components. It is stabilized to meet automotive heat ageing requirements (21 days at 150°C). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.70 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 101 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 79 | ||
| Shore D, 15 sec, 3.00 mm | 72 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 30.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 14 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 4300 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 25 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 230 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 132 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 81.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 8201-90 | ExxonMobil Chemical | TPV | Santoprene™ |
| Sylvin 9996-78 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Amilan® CM3516G33 | Toray Resin Company | Nylon Copolymer | Amilan® |
| GLAMIDE® T-422VOR | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |
| INNOPOL® PP CS 2-9120 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |