LNP™ THERMOCOMP™ UF004AS compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bgstr1_LNP-THERMOCOMP-UF004AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UF004AS is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1004AHS Product reorder name: UF004AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.20 to 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 136 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 7000 | MPa | ISO 178 |
| Flexural Stress | 178 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 256 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.1E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-301ML | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Gallonprene® GP520-3501 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Karina IVORY PVC COMPOUND -E 907-35/ 1-AY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 80-8030 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| PLUSTEK PD300G4 | Polyram Ram-On Industries | Nylon 12 | PLUSTEK |