Radilon® A ERV3012
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BgSvzt_Radilon-A-ERV3012.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA66 18% Glass Fiber reinforced injection moulding grade. High impact strength. Natural colour |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.21 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 6.7 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.8 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5300 | 4100 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 105 | 77.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.2 | 7.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/eA | |||
| -30°C | 9.5 | 10 | kJ/m² | ISO 179/eA |
| 23°C | 13 | 20 | kJ/m² | ISO 179/eA |
| Charpy Unnotched Impact Strength | ISO 179/eU | |||
| -30°C | 70 | -- | kJ/m² | ISO 179/eU |
| 23°C | 68 | 80 | kJ/m² | ISO 179/eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 240 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 210 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | -- | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | UL 94 | |
| 1.60 mm | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357-1-3 at a heating rate of 10°C/min. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline IS RDX 5235 F | Melos GmbH | TP, Unspecified | Mecoline |
| SWANCOR Epoxy 905-2 | SWANCOR IND. CO., LTD. | Epoxy | SWANCOR Epoxy |
| Nipol® SBR 1723 | Zeon Corporation | SBR, Emulsion | Nipol® SBR |
| LINATHENE® LL120C | USI Corporation | LLDPE | LINATHENE® |
| Sarlink® TPE ML-1140N NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |