Ateva® 1850A
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | Ateva® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Bf7qpc_Ateva-1850A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| This resin is commonly used for hot melt coating and adhesive applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.935 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 150 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 86 | ||
| Shore D | 34 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 7.00 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 700 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 42.0 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 84.0 | °C | ASTM D3418 |
| Ring and Ball Softening Point | 95 | °C | ASTM E28 |
| Note Message | |
|---|---|
| 1 . | Type IV, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1009 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| Shin-Etsu RTV KE-3418 | Shin-Etsu Silicones of America | Silicone Rubber, RTV-1 | Shin-Etsu RTV |
| Stat-Rite® M809 | Lubrizol Advanced Materials, Inc. | Acrylic, Unspecified | Stat-Rite® |
| WanBlend® WHT-HF8485K2 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | WanBlend® |
| Europrene Latice® 5584 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |