GAPEX® RPP30EB56BK
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BeQtP6_GAPEX-RPP30EB56BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GAPEX®RPP30EB56BK is a polypropylene homopolymer (PP Homopoly) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main features of the RPP30EB56BK are:
GAPEX®The typical application fields of RPP30EB56BK are: automobile industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.65 | % | ISO 294-4 |
| Flow direction | 0.65 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 71.9 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 5000 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180 | ||
| -40°C | 4.9 | kJ/m² | ISO 180 |
| 23°C | 6.8 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 142 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tensile/Izod Change, 1,000 hrs @ 140°C, ISO 188: +7/-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 80209 EM HS | RTP Company | Nylon 66 | RTP |
| Shanghai Ofluorine PVDF 9201 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| ShinkoLite-P IR G-504 | Mitsubishi Rayon America Inc. | Acrylic (PMMA) | ShinkoLite-P |
| LIHAN® A102 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 | LIHAN® |
| POCAN® KU 2-7241 000000 | LANXESS GmbH | PBT | POCAN® |