INSTRUC FEPGF10
| Category: | FEP , Perfluoroethylene Propylene Copolymer |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BdOohH_INSTRUC-FEPGF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| INSTRUC FEPGF10 is a Perfluoroethylene Propylene Copolymer (FEP) product filled with 10% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.17 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 29.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 3.0 to 5.0 | % | ASTM D638 |
| Flexural Modulus | 3310 | MPa | ASTM D790 |
| Flexural Strength | 47.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256 | |
| Unnotched Izod Impact | 1300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 153 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 2.40 | ||
| 1 MHz | 2.40 | ||
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 2.0E-3 | ||
| 1 MHz | 2.0E-4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 343 to 385 | °C | |
| Mold Temperature | 149 to 204 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M8190 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Alathon® H6030 | LyondellBasell Industries | HDPE | Alathon® |
| EVICOM™ GD1/774 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| Leona™ 1402G | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Karina RED PVC COMPOUND -E711D42/158-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |