PRL PCSF-FR1
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BcemLB_PRL-PCSF-FR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PCSF-FR1 is a Polycarbonate (PC) product filled with 10% glass fiber. It can be processed by structural foam molding and is available in North America. Typical application: Foam. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 65.5 | MPa | |
| Break, 3.18 mm | 63.1 | MPa | |
| Flexural Modulus (3.18 mm) | 3790 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 138 | °C | |
| RTI Elec (6.00 mm) | 80.0 | °C | UL 746 |
| RTI Imp (6.00 mm) | 80.0 | °C | UL 746 |
| RTI Str (6.00 mm) | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (6.00 mm, ALL) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 118 to 124 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 293 to 310 | °C | |
| Front Temperature | 293 to 310 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 104 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP FR 7380-8001 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| SABIC® PPcompound 108CSF10 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Alcryn® ALR FRC2 | Advanced Polymer Alloys | MPR | Alcryn® |
| Alpha PVC GW 2462-H VW1 NAT LCF | AlphaGary | PVC, Semi-Rigid | Alpha PVC |
| SQUARE® LSR6900-15A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |