UBESTA 3020 GX12
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | UBE Engineering Plastics, S.A. |
| Trademark: | UBESTA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BcKOiG_UBESTA-3020-GX12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UBESTA 3020 GX12 is a conductive fibre and glass fibre reinforced Polyamide 12 for injection moulding application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.60 | % | ISO 294-4 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 126 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ISO 178 |
| Flexural Stress | 188 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, complete fracture | 12 | kJ/m² | ISO 179/1eA |
| 23°C, complete fracture | 20 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 177 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 163 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 178 | °C | ISO 3146 |
| CLTE - Flow | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+6 | ohms·cm | IEC 60093 |
| Additional Information |
|---|
| The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.Volume Resistivity, IEC 60093: <1e6 ohm-cmAbrasion Loss, ISO 9352, CS-17, 1000 rev.: 12 mg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen 2152HOXP | LyondellBasell Industries | PP Homopolymer | Moplen |
| Wellamid® GS1861-N1(PTFE) | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| DJSilicone NE-7130 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Karina WHITE PVC COMPOUND E 854-10/144-ERYM | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 1199 A X 136859 B EG | RTP Company | PETG | RTP |