NOVAPOLY 0225UV
| Category: | PC Alloy , Polycarbonate Alloy |
| Manufacturer: | NOVA Polymers, Inc. |
| Trademark: | NOVAPOLY |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BbXuPz_NOVAPOLY-0225UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NOVAPOLY 0225UV is a Polycarbonate Alloy (PC Alloy) material. It is available in North America for injection molding. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (266°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm, Injection Molded) | 0.80 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 51.7 | MPa | ASTM D638 |
| Flexural Modulus 2(Injection Molded) | 2070 | MPa | ASTM D790 |
| Flexural Strength 3(Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 690 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm, Injection Molded | 107 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm, Injection Molded | 98.9 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKNIFLEX® VDC 200-25-40 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PE/PVDC | TEKNIFLEX® |
| Sylvin 2947-75 Clear 8392 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ELITE™ 5815P | The Dow Chemical Company | EPE | ELITE™ |
| EnCom HF ABS 7530 | EnCom, Inc. | ABS | EnCom |
| MAJORIS GFR307 - 8229 | AD majoris | PP, Unspecified | MAJORIS |