Ultrason® E Dimension E1010 G9
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BWwqML_Ultrason-E-Dimension-E1010-G9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity injection moulding grade with high rigidity and strength, 45 % glass fiber reinforced. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.73 | g/cm³ | ISO 1183 |
| Apparent Density | 0.70 to 0.80 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 35.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.40 | % | |
| Water Absorption (Saturation, 23°C) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 216 | °C | ISO 75-2/A |
| CLTE - Flow | |||
| 23 to 80°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| 180°C | 1.5E-5 | cm/cm/°C | DIN 53752 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 125 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 340 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENYL SWGB300H | AD majoris | Nylon 6 | VENYL |
| Toughblend® PP-1250 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Copolymer | Toughblend® |
| Karina PVC COMPOUND GRAY E-700N18/724-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |
| Polygen SG8A | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| LGH 314 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |