AT 505
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Celanese EVA Performance Polymers |
| Trademark: | AT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BVdgXS_AT-505.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A high strength resin, recommended for shrink films and general purpose packaging. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 150 µm | 200 | MPa | ASTM D882 |
| 1% secant, TD : 150 µm | 220 | MPa | ASTM D882 |
| Tensile Strength 1 | ASTM D882 | ||
| MD : Yield, 150 µm | 11.0 | MPa | ASTM D882 |
| TD : Yield, 150 µm | 11.0 | MPa | ASTM D882 |
| MD : Break, 150 µm | 21.0 | MPa | ASTM D882 |
| TD : Break, 150 µm | 21.0 | MPa | ASTM D882 |
| Tensile Elongation 2 | ASTM D882 | ||
| MD : Break, 150 µm | 580 | % | ASTM D882 |
| TD : Break, 150 µm | 670 | % | ASTM D882 |
| Dart Drop Impact 3(150 µm) | 300 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 112 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 150 µm) | 35 | ASTM D2457 | |
| Haze (150 µm) | 20 | % | ASTM D1003 |
| Additional Information |
|---|
| The value listed as Density-Specific Gravity, ASTM D1505, was tested in accordance with ASTM D1928 ProcC Mod. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 500 mm/min |
| 2 . | 500 mm/min |
| 3 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx TPP2B20 | The Matrixx Group, Inc. | PP Copolymer | Matrixx |
| RTP 2099 X 128018 B | RTP Company | PC+PBT | RTP |
| TAROLOX 10 Z2 | Taro Plast S.p.A. | PBT | TAROLOX |
| ESTAPROP 1040 V2 H | Cossa Polimeri S.r.l. | PP Homopolymer | ESTAPROP |
| HOPELEX PC-1220U | Lotte Chemical Corporation | PC | HOPELEX |