INEOS LDPE 21D430
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BSQdmW_INEOS-LDPE-21D430.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Applications 21D430 is particularly suitable for heavy duty film applications such as sacks, pallet shrink wrap and agricultural film. Characteristics 21D430 is an easily extrudable LDPE homopolymer. It offers the following properties:
If corona treatment is necessary, the level should normally be in the range 38-48N/m. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183/D |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.26 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | > 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 100 | µm | |
| Tensile Modulus | ISO 1184 | ||
| 1% secant, MD : 100 µm | 180 | MPa | ISO 1184 |
| 1% secant, TD : 100 µm | 180 | MPa | ISO 1184 |
| Tensile Stress | ISO 1184 | ||
| MD : Yield, 100 µm | 11.0 | MPa | ISO 1184 |
| TD : Yield, 100 µm | 11.0 | MPa | ISO 1184 |
| MD : 100 µm | 26.0 | MPa | ISO 1184 |
| TD : 100 µm | 25.0 | MPa | ISO 1184 |
| Tensile Elongation | ISO 1184 | ||
| MD : Break, 100 µm | 300 | % | ISO 1184 |
| TD : Break, 100 µm | 500 | % | ISO 1184 |
| Dart Drop Impact (100 µm) | 460 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 100 µm) | 40 | ASTM D2457 | |
| Haze (100 µm) | 15 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 240 - 280 | °C |
| Extrusion instructions |
|---|
| Cast Film Extruders: 240 to 280°CBlown Film Extruders: 160 to 185°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Westlake LDPE EC478AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| DENKA Polymer Alloy HS-G193 | Denka Company Limited | PC+ABS | DENKA Polymer Alloy |
| EMERGE™ PC/ABS 7350 | Trinseo | PC+ABS | EMERGE™ |
| Hifax CB 1128 A/1 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| HiFill® PA6 0254 B2 | Techmer Engineered Solutions | Nylon 6 | HiFill® |