VALOX™ V3902WX resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BQIcUr_VALOX-V3902WX-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PBT/PC blend - Unreinforced - Flame Retardant. This is a UV-stabilized grade designed for outdoor enclosure applications requiring UL 746C F1 weatherability performance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (265°C/2.16 kg) | 10.0 | cm³/10min | ISO 1133 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 51.0 | MPa | Internal Method |
| Yield 1 | 54.0 | MPa | ASTM D638 |
| Yield | 54.0 | MPa | ISO 527-2/50 |
| Break 2 | 42.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield 3 | 4.0 | % | ASTM D638 |
| Break | 130 | % | Internal Method |
| Break 4 | 38 | % | ASTM D638 |
| Break | 23 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2140 | MPa | ASTM D790 |
| -- 6 | 2260 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 82.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 77.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 51 | kJ/m² | |
| Notched Izod Impact (23°C) | 670 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 127 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 9 | 87.0 | °C | ISO 75-2/Af |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | 115 | °C | UL 746 |
| RTI Imp | 115 | °C | UL 746 |
| RTI Str | 115 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 3.00 mm | 5VA | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 3.00 mm 10 | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 3.00 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 260 | °C | |
| Processing (Melt) Temp | 249 to 266 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm | |
| Vent Depth | 0.025 to 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 mm |
| 10 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA250GM40 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| Moplen HP456H | LyondellBasell Industries | PP Homopolymer | Moplen |
| TPUCO® TPUI-L95 | Taiwan PU Corporation | TPU-Polyether | TPUCO® |
| Colorite G Series 8312G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Durethan® BKV 130 GIT DUS008 900116 | LANXESS Corporation | Nylon 6 | Durethan® |