Epiall® 1914A
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Epiall® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BQ9tvE_Epiall-1914A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epiall 1914A is a short fiberglass reinforced epoxy molding compound, with excellent dimensional stability, good strength properties and good electrical insulation properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.99 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 63 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 91.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 22000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 135 | MPa | ASTM D790 |
| Compressive Strength | 237 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 38 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, Compression Molded | 280 | °C | |
| 1.8 MPa, Annealed, Compression Molded | > 282 | °C | |
| CLTE | ASTM E831 | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 3.3E-5 | cm/cm/°C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 13 | kV/mm | |
| -- 3 | 12 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 4.50 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.40 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSC 6020 | Marco Polo International, Inc. | PS (GPPS) | MARPOL® PSC |
| Tenite™ Butyrate 285E0V16304 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Sylvin 9600-100 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9647-48 Clear Blue 1836 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ GX94043L compound | SABIC Innovative Plastics Europe | PSU | LNP™ THERMOCOMP™ |