Chemlon® 66GS6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BPsmFF_Chemlon-66GS6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 66GS6 is a nylon 66 containing 30% glass beads, which can provide greater rigidity and less deformability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.80 - 1.0 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.80 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4000 | 2000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 - 10 | 20 - 50 | % | ISO 527-2 |
| Flexural Modulus | 2800 | 1100 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | |||
| -- 1 | 130 | -- | MPa | ISO 178 |
| -- 2 | -- | 63.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 3.0 | 9.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 23 kJ/m² | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 220 | 210 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.0 | 70.0 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 17 | 11 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.60 | 4.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.010 | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| 如果材料在空气中暴露的时间不超过3小时，则无需干燥。背压：低注射压力：高 |
| Note Message | |
|---|---|
| 1 . | At break |
| 2 . | At Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene Aceso® PPM R021 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Vydyne® 49H | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| DURACON® JW-03 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| Elastron® G G103.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| IROCOAT® CA-236 | Huntsman Corporation | TPU, Unspecified | IROCOAT® |