RESOLE FM 4029F-1
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | RESOLE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BPp4v7_RESOLE-FM-4029F-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FM 4029F-1 is a fiberglass and mineral reinforced phenolic molding compound, with excellent dimensional stability and good strength at elevated temperatures. Automatic performing is enhanced by the high powder density. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 60.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 20000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 110 | MPa | ASTM D790 |
| Compressive Strength | 210 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 243 | °C | ASTM D648 |
| CLTE - Flow | 1.3E-5 | cm/cm/°C | ASTM E831 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | UL 94 | |
| 3.18 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 | °C | |
| Middle Temperature | 73.9 | °C | |
| Nozzle Temperature | 87.8 | °C | |
| Processing (Melt) Temp | 98.9 - 116 | °C | |
| Mold Temperature | 166 - 188 | °C | |
| Injection Pressure | 100 - 248 | MPa | |
| Holding Pressure | 30.0 - 89.6 | MPa | |
| Back Pressure | 4.83 - 15.2 | MPa |
| Injection instructions |
|---|
| Plastication: 50rpmInjection Time: 2 to 8 secHold Time: 1 to 5 sec/mmCure Time, 0.125 in: 5 to 12 sec/mmAll ASTM properties listed were tested in accordance with ASTM D5948.Powder Density, ASTM D1895: 1 g/cm³Water Absorption, ASTM D570, 48 hrs, 50°C: 0.15%DTUL @264psi - Unannealed, ASTM D648, Post Baked, Compression Molded: >282°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ CPVC EC050 | PolyOne Corporation | CPVC | Geon™ CPVC |
| Innova R 830D | Innova SA | PS (HIPS) | Innova |
| Karina BEIGE PVC COMPOUND -E 841-08/184-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina WHITE PVC COMPOUND 901D10/146-B-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RONFALIN® ABS 1353 A | A. Schulman Europe | ABS | RONFALIN® |