LNP™ STAT-LOY™ A3000T compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BNQLou_LNPSTATLOYA3000Tcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON A3000T is a compound based on Acrylonitrile Butadiene Styrene resin. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound A-CLEAR Product reorder name: A3000T |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 28.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 25 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 1200 | MPa | ISO 178 |
| Flexural Stress | 37.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 69.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+11 | ohms | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 10 SE A | RTP Company | PC | RTP |
| Sarlink® TPE ML-2355B | Teknor Apex Company | TPE | Sarlink® TPE |
| Evoprene™ G 970 | AlphaGary | SEBS | Evoprene™ G |
| Formolon® KVF | Formosa Plastics Corporation, U.S.A. | PVC Homopolymer | Formolon® |
| PermaStat® 100 LE | RTP Company | PP, Unspecified | PermaStat® |