Badatron® PPS GF30
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Bada AG |
| Trademark: | Badatron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BNCEaL_BadatronPPSGF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS-GF30, 30% glass fibres reinforced injection moulding grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.52 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 12000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 140 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 1.6 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 2(23°C) | 37 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 4.00 mm) | 255 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 295 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 5(1.00 mm) | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity 6(1.00 mm) | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index 7(1.00 mm) | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-0 | UL 94 | |
| 1.6 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.75 mm | 960 | °C | IEC 60695-2-12 |
| 1.6 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.75 mm | 960 | °C | IEC 60695-2-13 |
| 1.6 mm | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Maximum Service Temperature, IEC 216, some hours: 260°CMaximum Service Temperature, IEC 216, 20000 hours: 210°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 300 - 340 | °C | |
| Mold Temperature | 140 - 180 | °C |
| Note Message | |
|---|---|
| 1 . | 80x10x4 mm |
| 2 . | 80x10x4 mm |
| 3 . | 110x10x4 mm |
| 4 . | Compound for molding, 10k/min |
| 5 . | 80x80x1 mm |
| 6 . | 80x80x1 mm |
| 7 . | 80x80x1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2205 HF TFE 15 Z | RTP Company | PEEK | RTP |
| Sylvin 9639-83AM Clear 8354 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| CYCOLAC™ BDT5510 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| Generic PUR, Unspecified - Carbon Fiber | Generic | PUR, Unspecified | Generic |
| IDI STC 2252 | IDI Composites International | Polyester, TS | IDI STC |