CERTENE™ HWB-1051
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Muehlstein |
| Trademark: | CERTENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BMCSeK_CERTENE-HWB-1051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HWB-1051 is a certified prime grade Hexene copolymer High Molecular Weight developed for BLOW MOLDING of high performance medium to large size industrial containers. HWB-1051 features good processability, good melt strength, excellent combination of ESCR, high Impact strength, Stiffness, good Thermoform ability, and good chemical resistance. HWB-1051 applications include 20 to 55 gallon containers, chemical and gasoline tanks, carrying cases, automotive parts, tool boxes, truck-bed liners, and sheet, pipe and profile extrusion. HWB-1051 recommended processing temperature is 190 to 210°C.. HWB-1051 complies with FDA regulation 21CFR 177.1520 (c )3.1(a) + 3.2 (a) and with most international regulations concerning the use of Polyethylene in contact with food articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.951 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | |
| 190°C/21.6 kg | 10 | g/10 min | |
| Environmental Stress-Cracking Resistance | |||
| Compression Molded, F50 | > 1000 | hr | ASTM D1693 |
| 50°C, 1.75 mm, 10% Igepal, Compression Molded, F50 | 150 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 3(Compression Molded) | 1070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength (Compression Molded) | 347 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 44.0 | °C | ASTM D648 |
| Brittleness Temperature | < -90.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature | 190 to 210 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADENE GHFAG | A.D. Compound spa | PP Copolymer | ADENE |
| Grivory® XE 4120 black 9916 | EMS-GRIVORY | Nylon 10T/X | Grivory® |
| HiFill® ABS GF60 BK | Techmer Engineered Solutions | ABS | HiFill® |
| LNP™ THERMOCOMP™ KZ002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| LNP™ THERMOCOMP™ JF004EXP compound | SABIC Innovative Plastics | PESU | LNP™ THERMOCOMP™ |