Desmopan® 192
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BKmHod_Desmopan-192.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; with high mechanical strength for articles subject to wear; Application; Shift lever balls; Roller tires; Coupling elements; Shoe heels |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1230 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 94 | ||
| Shore D, 15 sec | 41 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504 | ||
| Break, 23°C | 49.3 | MPa | |
| 10% Strain, 23°C 3 | 4.50 | MPa | |
| 50% Strain, 23°C 4 | 8.40 | MPa | |
| 100% Strain, 23°C 5 | 9.90 | MPa | |
| 300% Strain, 23°C 6 | 19.5 | MPa | |
| Tensile Strain 7(Break, 23°C) | 550 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 30.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 450 | MPa | |
| 20°C | 93.0 | MPa | |
| 60°C | 48.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 30 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 8 | 100 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 25 | % | |
| 70°C, 24 hr | 60 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 90.0 | °C | |
| Processing (Melt) Temp | 210 to 225 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 200 mm/min |
| 6 . | 200 mm/min |
| 7 . | 200 mm/min |
| 8 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Accura® Peak™ | 3D Systems | Epoxy | Accura® |
| Hiprolon® 11 ECN Blue H8L | Arkema | Nylon 1012 | Hiprolon® |
| KOPA® KN170SA | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| LNP™ LUBRICOMP™ IL004 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| ULTEM™ 2100F resin | SABIC Innovative Plastics Europe | PEI | ULTEM™ |