Plexiglas® HFI10
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BH0IyB_Plexiglas-HFI10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® HFI10 is an impact modified thermoplastic acrylic resin formulated for injection molding. It has high melt flow, enhanced mold release properties and provides 10 times the impact resistance of standard acrylics while maintaining excellent optical properties. It offers an excellent balance between melt flow and increased resistance to breakage, while providing weatherability superior to that provided by other high-impact plastics. Supplemental moldflow simulation data is available. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.3 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 38 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1860 | MPa | ASTM D638 |
| Tensile Strength (Break) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 50 | % | ASTM D638 |
| Flexural Modulus | 1860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 88.9 | °C | |
| 1.8 MPa, Annealed | 79.4 | °C | |
| Vicat Softening Temperature | |||
| -- | 93.9 | °C | ASTM D1525 2 |
| -- | 82.8 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.22 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 4 | 1.490 | ASTM D542 | |
| Transmittance (3180 µm) | 90.0 | % | ASTM D1003 |
| Haze (3180 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0231V2 | ASTM D788 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 87.8 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 50 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 221 | °C | |
| Middle Temperature | 227 | °C | |
| Front Temperature | 232 | °C | |
| Nozzle Temperature | 227 | °C | |
| Processing (Melt) Temp | < 271 | °C | |
| Mold Temperature | 37.8 to 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.689 | MPa | |
| Screw Speed | 50 to 100 | rpm | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 | ||
| Screw Compression Ratio | 2.0:1.0 to 2.5:1.0 | ||
| Vent Depth | 0.051 | mm |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| 4 . | ND @ 72°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® B50L 01 | BASF Corporation | Nylon 6 | Ultramid® |
| AKROMID® B3 GFM 15/25 black (1312) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Karina IVORY PVC COMPOUND IRDB 40-LF-BR(CABELAUTO) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KumhoSunny PC 2501FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |
| K-vinyl KSF-54 | Technovinyl Polymers India Ltd. | PVC, Flexible | K-vinyl |