TOTAL Polystyrene Crystal CX5243

Category:	PS (GPPS) , General Purpose Polystyrene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polystyrene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BGlSaA_TOTAL-Polystyrene-Crystal-CX5243.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
TOTAL Petrochemicals CX5243 is a very high flow, high heat crystal polystyrene. The very low viscosity of this grade combined with its high heat resistance makes it particularly suitable for the production of extrusion foam board (XPS) with blowing agents such as CO 2 and HFC. It is also ideal for use as a masterbatch carrier. Applications Insulation foam board Masterbatch carrier Modifier for thermoplastic elastomers and rubbers General Information This material complies with FDA requirements as described in 21 CFR §177.1640. USP Class VI Material Safety Data Sheets are available to help customers satisfy their safety needs.

Message

TOTAL Petrochemicals CX5243 is a very high flow, high heat crystal polystyrene. The very low viscosity of this grade combined with its high heat resistance makes it particularly suitable for the production of extrusion foam board (XPS) with blowing agents such as CO 2 and HFC. It is also ideal for use as a masterbatch carrier.

Applications

Insulation foam board

Masterbatch carrier

Modifier for thermoplastic elastomers and rubbers

General Information

This material complies with FDA requirements as described in 21 CFR §177.1640.

USP Class VI

Material Safety Data Sheets are available to help customers satisfy their safety needs.

General Information
Features	High Flow High Heat Resistance Highly Crystalline Low Viscosity
Uses	Foam Masterbatch
Agency Ratings	FDA 21 CFR 177.1640 USP Class VI
Forms	Pellets
Processing Method	Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	23	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.40 to 0.70	%	ASTM D955
Moisture	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2960	MPa	ASTM D638
Tensile Strength	27.6	MPa	ASTM D638
Flexural Modulus	3310	MPa	ASTM D790
Flexural Strength	46.2	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Annealed)	95.6	°C	ASTM D648
Vicat Softening Temperature	106	°C	ASTM D1525

Resin Grade	Manufacturer	Category	Trademark
Moplen RP241R	LyondellBasell Industries	PP Random Copolymer	Moplen
Nypol® PA A3 G43 HS UV RH PRTA011 NR424	Petropol Industry and Trade of Polymers LTDA	Nylon 66	Nypol® PA
Bergadur™ PB40 GK30 BK002	PolyOne Corporation	PBT	Bergadur™
Fainplast PVC KL 94	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Durepol® PBT A3 G15 TZ NTLA010 BT327	Petropol Industry and Trade of Polymers LTDA	PBT	Durepol® PBT