LNP™ LUBRICOMP™ IAL12 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BGMsSG_LNPLUBRICOMPIAL12compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IAL12 is a compound based on Nylon 6/12 resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound IAL-4012 Product reorder name: IAL12 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3150 | MPa | ASTM D638 |
| Tensile Strength (Break) | 73.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 7.2 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 440 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 109 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI H K1416 | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| EvoSource™ ABS 4136 | MBA Polymers | ABS | EvoSource™ |
| KMI PP KM011-B | KMI Group, Inc. | PP Homopolymer | KMI PP |
| Taizhou Plastic PA-A4-1 | Taizhou Plastic Co., Ltd. | Nylon 66 | Taizhou Plastic |
| Sinkral® M 4 Modena | Versalis S.p.A. | ABS | Sinkral® |