Silastic® Q7-4550

Category:	Silicone , Silicone
Manufacturer:	Dow Corning Corporation
Trademark:	Silastic®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BENa87_SilasticQ74550.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure APPLICATIONS SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices. DESCRIPTION SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization. The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses. After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

Message

Enhanced Tear Resistant (ETR) High Consistency Rubber silicone elastomers for peroxide cure

APPLICATIONS
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are uncatalyzed elastomer materials designed for compounding into elastomer for part fabrication and medical devices.

DESCRIPTION
SILASTIC BioMedical Grade ETR Elastomers (Q7-4535, Q7-4550, Q7-4565) are a series of one-part uncatalyzed silicone elastomer raw materials. The addition of a peroxide catalyst is necessary to accomplish vulcanization.

The resulting elastomers range in hardness from soft to firm (nominally 35 to 65, Shore A Durometer). These materials may be blended if desired to achieve intermediate hardnesses.

After appropriate compounding with a peroxide catalyst, cure and post-cure, the elastomers are heat stable up to 204°C (400°F), can be autoclaved, and exhibit high gas permeability compared with most thermoset elastomers and thermoplastics.

General Information
Features	High Gas Permeability High pressure heating resistance
Uses	Composite Medical/nursing supplies
Agency Ratings	EP Unspecified Rating ISO 10993-Part I USP Class VI
Processing Method	Composite

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.16	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	51		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (200% Strain)	2.30	MPa	ASTM D412
Tensile Strength	10.1	MPa	ASTM D412
Tensile Elongation (Break)	660	%	ASTM D412
Tear Strength ¹	30.0	kN/m	ASTM D624

Additional Information
Values are for samples crosslinked with Perkadox PD-505.

Note Message
1 .	B mould

Resin Grade	Manufacturer	Category	Trademark
Quantum Composites QC-8852	Quantum Composites Inc.	Vinyl Ester	Quantum Composites
ALAMID® 6.6 GF 30 MOD WL SCHWARZ-9665	LEIS Polytechnik - polymere Werkstoffe GmbH	Nylon 66	ALAMID®
Andur 5-DP-LM/Curene® 3005	Anderson Development Company	PUR-Ester/TDI	Andur
Kingfa JH-R2G10 P60	Kingfa	PC+ABS	Kingfa
3M™ Dyneon™ Perfluoroelastomer PFE 7502BZ	3M Advanced Materials Division	Perfluoroelastomer	3M™ Dyneon™ Perfluoroelastomer