ISPLEN® PM 270 BV
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BEHViB_ISPLEN-PM-270-BV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer, 20% mineral fillers reinforced and high melt flow rate. ISPLEN® PM270 BV gives a high stiffness, and a low warpage and shrinkage behaviour. This product is high heat and UV stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 0.93 to 0.97 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 73 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 32.0 | MPa | |
| Break | 25.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 5.0 | % | |
| Break | 22 | % | |
| Flexural Modulus | 2600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -20°C | 1.5 | kJ/m² | |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 2.7 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| -20°C | 11 | kJ/m² | |
| 0°C | 15 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 109 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 153 | °C | ISO 306/A120 |
| -- | 95.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® XPP 511 | Solvay Specialty Polymers | PTFE | Polymist® |
| Shinko-Lac® ASA S511 | Mitsubishi Rayon America Inc. | ASA | Shinko-Lac® |
| Wanthane® WHT-1585 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| Hostalen PP H1022 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| Sylvin 5175-92 White 1470 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |