Radilon® A 38 100 NAT
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BCNX1e_Radilon-A-38-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 high viscosity extrusion grade. Natural colour. Suitable for extrusion of tubes, profiles, bars, rods and sheets. Also suitable for injection moulding of high thickness items. ISO 1043 : PA66 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 8.4 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 2.1 | -- | % | |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 240 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3250 | 1600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 90.0 | 60.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 50 | > 50 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2980 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 105 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 8.0 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 195 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 240 | -- | °C | ISO 306/B50 |
| Melting Temperature | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 270 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RC240 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| APEX® 88-N051-A | Teknor Apex Company | PVC, Flexible | APEX® |
| Cri-Line GP-615-65-LV | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Iupiace® LN30 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina IVORY PVC COMPOUND 105471-35/1-Y-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |