RTP ESD C 1700
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BBy3Uy_RTP-ESD-C-1700.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3310 | MPa | ASTM D638 |
| Tensile Strength | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 2900 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 93.3 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 6mil/in.Tensile Elongation, ASTM D638: 3-5%NFPA Code 56A, Static Decay, FTMS-4046, 0.5 sec: Passes |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 - 260 | °C | |
| Middle Temperature | 204 - 260 | °C | |
| Front Temperature | 204 - 260 | °C | |
| Mold Temperature | 37.8 - 93.3 | °C | |
| Injection Pressure | 68.9 - 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® TP 11270 | Premix Oy | HDPE | PRE-ELEC® |
| SCANAMID 6 B11^ F50 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| 3M™ Dyneon™ Fluoroplastic ET 6235Z | 3M Advanced Materials Division | ETFE | 3M™ Dyneon™ Fluoroplastic |
| Generic Acetal (POM) Copolymer - Carbon Fiber | Generic | Acetal (POM) Copolymer | Generic |
| Iupilon® GSH2020DT 9010 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |