Thermec™ 4140R40
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Technical Polymers, LLC |
| Trademark: | Thermec™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BBpcGA_Thermec-4140R40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Thermec™4140R40 is a polyphenylene sulfide (PPS) material, which contains a 40% glass fiber reinforced material. This product is available in North America and is processed by injection molding. Thermec™The main features of 4140R40 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.66 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 17.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 13400 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 276 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 270 | °C | ASTM D648 |
| Melting Temperature | 280 | °C | DSC |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Volum Resistivity, ASTM D257: >1e13 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 - 149 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 316 - 343 | °C | |
| Mold Temperature | 135 - 149 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.103 - 0.689 | MPa | |
| Screw Speed | 100 | rpm | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 6.35 - 12.7 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SR257M | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| TEKNIFLEX® VDC 250-40 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PVDC | TEKNIFLEX® |
| Badamid® LA70 GF15 | Bada AG | Nylon 66 | Badamid® |
| KOCETAL® K100 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |
| POLIGOM G/35 | Crosspolimeri S.p.A. | EPDM | POLIGOM |