Plenco 06401 (Transfer)
| Category: | Phenolic , Phenolic |
| Manufacturer: | Plastics Engineering Co. |
| Trademark: | Plenco |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BBM2OS_Plenco-06401-Transfer-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PLENCO 06401 is a glass fiber and mineral filled two-stage phenolic molding compound. UL recognized under component file E40654. 06401 is available in black. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | ASTM D792 |
| Apparent Density | 0.70 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ASTM D638 |
| Tensile Strength | 118 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 16600 | MPa | ASTM D790 |
| Flexural Strength | 197 | MPa | ASTM D790 |
| Compressive Strength | 283 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 57.9 | J/m | ASTM D256 |
| Notched Izod Impact | 58 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 274 | °C | ASTM D648 |
| Continuous Use Temperature | 236 | °C | ASTM D794 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.2E+11 | ohms·cm | ASTM D257 |
| Dielectric Strength | ASTM D149 | ||
| -- 1 | 13 | kV/mm | ASTM D149 |
| -- 2 | 8.6 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.035 | ASTM D150 | |
| Arc Resistance | 63.0 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 175 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Additional Information |
|---|
| The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.05%Drop Ball Impact, PLENCO Method: 342 J/m |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 165 - 182 | °C | |
| Back Pressure | 0.300 | MPa | |
| Screw Speed | < 60 | rpm |
| Injection instructions |
|---|
| Transfer Time: 3-8 secTransfer Pressure: 5.5-6.9 MPaPreheating Temperature: 104-115°C |
| Note Message | |
|---|---|
| 1 . | Method A (short time) |
| 2 . | Method B (step by step) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (PMMA) M/06 | A. Schulman Europe | Acrylic (PMMA) | POLYMAN® |
| POLYPRO® HF5103 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Veradel® AG-330 | Solvay Specialty Polymers | PESU | Veradel® |
| Nipol® NBR DN202 | Zeon Corporation | NBR | Nipol® NBR |
| INEOS LLDPE LL6208AF | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |