SCHULAMID® 6 GBF 3010 H
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | BBCz7L_SCHULAMID-6-GBF-3010-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fiber and glass bead reinforced Polyamide 6 with higher stiffness and dimension stability |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.35 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 175 | 115 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 6000 | 3000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 110 | 55.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.5 | 12 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | -- | kJ/m² | |
| 23°C | 4.0 | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 35 | 90 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 190 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 218 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (115°C) | Pass | -- | IEC 60695-10-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | < 100 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 102 Z | RTP Company | PP, Unspecified | RTP |
| VICTREX® PEEK 450CA40 | Victrex plc | PEEK | VICTREX® PEEK |
| Chiao Fu PA6 MC312G40 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| Halene H M5018L | Haldia Petrochemicals Ltd. | HDPE | Halene H |
| CERTENE™ HI-1752 | Muehlstein | HDPE | CERTENE™ |