Teflon® FEP TE-9568

Category:	FEP , Perfluoroethylene Propylene Copolymer
Manufacturer:	DuPont Fluoropolymers
Trademark:	Teflon® FEP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	BA9t2q_Teflon-FEP-TE-9568.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Description DuPont™ Teflon ® FEP TE-9568 fluoropolymer resin is a negatively charged, hydrophobic colloid containing approximately 54% (by total weight) of 0.1 to 0.30 µm fluorinated ethylene propylene (FEP) particles suspended in water. It also contains approximately 6% (by weight of FEP resin) of a nonionic wetting agent and stabilizer. Color is off-white and nominal pH is 10.0. Viscosity at room temperature is approximately 25 cP. Teflon ® TE-9568 is a general-purpose dispersion. It can be used to impart some of the unique properties of Teflon ® FEP resin to end products that would be difflcult to make using traditional melt extrusion processes. It can be used to coat or impregnate porous structures or to make thin ?lms. It can be coated and melt bonded to polytetrafluoroethylene (PTFE) resin or used as a hot melt adhesive. The Teflon ® FEP resin in TE-9568 is a true thermoplastic, providing superior properties typical of the fluoropolymer resins: retention of properties after service at 204°C (400°F), useful properties at -240°C (-400°F), chemical inertness to nearly all industrial chemicals and solvents, and excellent dielectric properties. Refer to Table 1 for typical property data. Typical End Products Teflon ® FEP TE-9568 is suitable for many end products, including: heat-sealable top coatings for PTFE-coated fabrics used for belting, circuit boards, or electrical insulation; cast film for capacitors or chemical barriers; and as a hot melt adhesive for bonding molded PTFE or FEP parts to themselves or to each other.

Message

Description
DuPont™ Teflon ® FEP TE-9568 fluoropolymer resin is a negatively charged, hydrophobic colloid containing approximately 54% (by total weight) of 0.1 to 0.30 µm fluorinated ethylene propylene (FEP) particles suspended in water. It also contains approximately 6% (by weight of FEP resin) of a nonionic wetting agent and stabilizer. Color is off-white and nominal pH is 10.0. Viscosity at room temperature is approximately 25 cP.

Teflon ® TE-9568 is a general-purpose dispersion. It can be used to impart some of the unique properties of Teflon ® FEP resin to end products that would be difflcult to make using traditional melt extrusion processes. It can be used to coat or impregnate porous structures or to make thin ?lms. It can be coated and melt bonded to polytetrafluoroethylene (PTFE) resin or used as a hot melt adhesive.

The Teflon ® FEP resin in TE-9568 is a true thermoplastic, providing superior properties typical of the fluoropolymer resins: retention of properties after service at 204°C (400°F), useful properties at -240°C (-400°F), chemical inertness to nearly all industrial chemicals and solvents, and excellent dielectric properties. Refer to Table 1 for typical property data.

Typical End Products
Teflon ® FEP TE-9568 is suitable for many end products, including: heat-sealable top coatings for PTFE-coated fabrics used for belting, circuit boards, or electrical insulation; cast film for capacitors or chemical barriers; and as a hot melt adhesive for bonding molded PTFE or FEP parts to themselves or to each other.

General Information
Features	Food Contact Acceptable Good Chemical Resistance Good Electrical Properties
Uses	Adhesives Cast Film Coating Applications Film
Agency Ratings	FDA 21 CFR 177.1550 2
Appearance	Off-White
Forms	Dispersion
Processing Method	Dip Coating

Physical	Nominal Value	Unit	Test Method
Density	1.41	g/cm³	ISO 8962
Melt Mass-Flow Rate (MFR) (372°C/5.0 kg)	7.0	g/10 min	ASTM D2116, ISO 12086
Solution Viscosity
--	25	mPa·s	ISO 2555
--	25	mPa·s	ASTM D2196
Average Particle Size	180	nm
pH
--	10.0		ASTM E70
--	10.0		ISO 1148
Solids Content
--	54	%	ASTM D4441
--	54	%	ISO 12086
Weight - dry	760	kg/m³

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	260	°C	ASTM D2116

Resin Grade	Manufacturer	Category	Trademark
Xuchuan XCW-8060SC	Xuchuan Chemical (Suzhou) Co., Ltd	PUR, Unspecified	Xuchuan
NuSil MED-6340	NuSil Technology	Silicone	NuSil
HiFill® PP 0225 B	Techmer Engineered Solutions	PP, Unspecified	HiFill®
Hipolyene 3020 HC RM	Zylog Plastalloys	TPO (POE)	Hipolyene
Lupoy® 1302HP-22	LG Chem Ltd.	PC	Lupoy®