SUMIKASUPER® LCP E6109F
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Sumitomo Chemical Co., Ltd. |
| Trademark: | SUMIKASUPER® LCP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B9uGz2_SUMIKASUPER-LCP-E6109F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SUMIKASUPER LCP is a thermotropic liquid crystalline polyester, showing the highest heat resistance among engineering plastics. SUMIKASUPER LCP E6109F is a sliding grade that contains an inorganic filler and fluororesin. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.80 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow | 0.25 | % | |
| Across Flow | 1.2 | % | |
| Water Absorption (Saturation) | 0.020 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 126 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 11500 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (6.40 mm) | 380 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 270 | °C | ASTM D648 |
| CLTE | Internal Method | ||
| Flow : 150°C | 1.4E-5 | cm/cm/°C | |
| Transverse : 150°C | 7.8E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm, BK) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Soldering Resistance | 300 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 150 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 300 to 320 | °C | |
| Middle Temperature | 320 to 350 | °C | |
| Front Temperature | 340 to 370 | °C | |
| Nozzle Temperature | 340 to 370 | °C | |
| Processing (Melt) Temp | 350 | °C | |
| Mold Temperature | 70.0 to 160 | °C | |
| Injection Pressure | 78.0 to 157 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 20.0 to 39.0 | MPa | |
| Back Pressure | 0.980 to 4.90 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SFW6500A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| alphalon™ 27 | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Americas Styrenics EA3400 | Americas Styrenics LLC | PS (GPPS) | Americas Styrenics |
| Ferro PP TPP20AD59HB-NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Westlake LDPE EF 311 | Westlake Chemical Corporation | LDPE | Westlake LDPE |