LUVOCOM®70-9045 is a Polyketone (PK) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 70-9045 are: Conductivity anti-warping Good stiffness chemical resistance Hydrolytic stability LUVOCOM®The typical application fields of 70-9045 are: engineering/industrial accessories

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Low warpage Rigid, good Static conduction Good strength Good chemical resistance Hydrolysis stability
Uses	Cam
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.33	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/2.16 kg)	15.0	cm³/10min	ISO 1133
Molding Shrinkage	0.20 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	9000	MPa	ISO 527-2
Tensile Stress (Break)	130	MPa	ISO 527-2
Tensile Strain (Yield)	4.5	%	ISO 527-2
Flexural Modulus	7500	MPa	ISO 178
Flexural Stress	190	MPa	ISO 178
Flexural Strain at Flexural Strength	5.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	150	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	11	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	55	kJ/m²	ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	208	°C	ISO 75-2/A
Continuous Use Temperature	110	°C	UL 746B
Vicat Softening Temperature	204	°C	ISO 306/A
CLTE - Flow	6.0E-5	cm/cm/°C	DIN 53752
Thermal Conductivity	0.40	W/m/K	DIN 52612

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+6	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
Hot air dryer	120	°C
Hot air dryer, B	80	°C
Drying Time
Hot air dryer	1.0 - 4.0	hr
Hot air dryer, B	2.0 - 6.0	hr
Rear Temperature	230 - 250	°C
Middle Temperature	230 - 260	°C
Front Temperature	240 - 260	°C
Nozzle Temperature	250 - 265	°C
Processing (Melt) Temp	245	°C
Mold Temperature	60 - 100	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms

Category:	PK , Polyketone
Manufacturer:	LEHVOSS Group
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	B9iUGn_LUVOCOM709045.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Maxelast® A9730	Nantong Polymax Elastomer Technology, Co., Ltd	TPE	Maxelast®
Sylvin 6209-75 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Trilene FreeFlow™ CP1100	Lion Copolymer, LLC	EPM	Trilene FreeFlow™
ORTHTEK® WF	Greene, Tweed & Co.	PEEK	ORTHTEK®
Pebax® 4033 SA 01 MED	Arkema	PEBA-Ether	Pebax®