Iupilon® GSH2020DR 9913A
| Category: | PC , Polycarbonate |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Iupilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B932kZ_Iupilon-GSH2020DR-9913A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Iupilon® GSH2020DR 9913A is a Polycarbonate (PC) material filled with 20% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Iupilon® GSH2020DR 9913A are:
Typical application of Iupilon® GSH2020DR 9913A: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.6 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 6.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Across Flow : 3.20 mm | 0.30 to 0.50 | % | |
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Water Absorption (Saturation, 23°C) | 0.11 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6200 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 86.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 5500 | MPa | ISO 178 |
| Flexural Stress | 141 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 43 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 6.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.400 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 270 to 290 | °C | |
| Middle Temperature | 280 to 300 | °C | |
| Front Temperature | 290 to 310 | °C | |
| Nozzle Temperature | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Pressure | 50.0 to 150 | MPa | |
| Screw Speed | 50 to 100 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® EL-3800E | Sumitomo Bakelite Co., Ltd. | Epoxy | SUMILITE® |
| Keliren® CM2535 | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |
| LONGLITE® PBT 3030-104FR | CCP Group | PBT | LONGLITE® PBT |
| Plaslube® PA6 TS18 | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Sylvin 8260-90FUV White 1572 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |