LEXAN™ FXD171R resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B8Gxq9_LEXAN-FXD171R-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Transparent/transluscent PC for light diffusion special effects. MFR of 25.0. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2330 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.1 | MPa | |
| Break | 64.1 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.2 | % | |
| Break | 130 | % | |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 780 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 70.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 127 | °C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.09 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 260 to 282 | °C | |
| Front Temperature | 271 to 293 | °C | |
| Nozzle Temperature | 266 to 288 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.0 to 93.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH 810HF | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Guang Sung PVC GPMD70 | Guang Sung Plastics (GSPL) | PVC, Rigid | Guang Sung PVC |
| Karina COMP. PVC BRANCO -E 703D10/ 58-H-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina BLACK PVC COMPOUND 900D48/ 1-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYCOMPO PE SP2040 | POLYCOMPO Co.,Ltd. | LLDPE | POLYCOMPO PE |