EVAL™ L171B
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | EVAL Europe nv |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B5R7KL_EVAL-L171B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EVAL™ L171B is an Ethylene Vinyl Alcohol (EVOH) product. It is available in Europe. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 210°C/2.16 kg | 4.0 | g/10 min | |
| 230°C/2.16 kg | 7.1 | g/10 min | |
| 250°C/2.16 kg | 11 | g/10 min | |
| Ethylene Content | 27.0 | mol% | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 95 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 13 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability 1 | ISO 14663-2 | ||
| 20°C, 0% RH | 2.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 35% RH | 2.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 4.0E-3 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.024 | cm³·mm/m²/atm/24 hr | |
| 20°C, 90% RH | 0.052 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 2 | 1.9 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -- | 2.0 | kJ/m² | |
| -40°C | 2.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 60.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 177 | °C | ISO 306 |
| Melting Temperature | 191 | °C | ISO 11357-3 |
| Peak Crystallization Temperature | 164 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Annex C |
| 2 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A USZ200 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| Small Boss SPVC8014 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Unspecified | Small Boss |
| Unipren® Elastomers B3 NTLA010 75A UP311 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Hostacom TRC 454N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Loyblend® TA-1810FR | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PC+ABS | Loyblend® |