INTEGRAL™ D200

Category:	Polyolefin, Unspecified , Polyolefin Adhesive Film
Manufacturer:	The Dow Chemical Company
Trademark:	INTEGRAL™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	B4uq8O_INTEGRAL-D200.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
INTEGRAL™ D200 Polyolefin Adhesive Film is a heat-activated adhesive film designed for bonding to polyurethane foam to provide a liquid barrier for carpet underlayment and other applications. This film has a low heat activation point on one side of the film with a non-adhesive layer on the other side to minimize the film sticking to the hot roller surface during lamination. New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative General Characteristics: Heat Activation Point: 205 °F (96 °C) Thickness: 1.75 to 2.50 mil (45-65 µm) Width: 73 in. (1855 mm) Color: Blue, Red, White, and Yellow Treat: Treated Outside

Message

INTEGRAL™ D200 Polyolefin Adhesive Film is a heat-activated adhesive film designed for bonding to polyurethane foam to provide a liquid barrier for carpet underlayment and other applications. This film has a low heat activation point on one side of the film with a non-adhesive layer on the other side to minimize the film sticking to the hot roller surface during lamination.

New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative

General Characteristics:

Heat Activation Point: 205 °F (96 °C)

Thickness: 1.75 to 2.50 mil (45-65 µm)

Width: 73 in. (1855 mm)

Color: Blue, Red, White, and Yellow

Treat: Treated Outside

General Information
Appearance	Blue Red White Yellow
Forms	Film

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	44	µm	ASTM D374
Film Thickness - Recommended / Available	1.75-2.50 mil (45-65 µ)
Secant Modulus			ASTM D882
2% Secant, MD	259	MPa
2% Secant, TD	225	MPa
Tensile Strength			ASTM D882
MD : Yield	14.1	MPa
TD : Yield	12.1	MPa
MD : Break, 44 µm	33.0	MPa
TD : Break	25.2	MPa
Tensile Elongation			ASTM D882
MD : Yield	16	%
TD : Yield	14	%
MD : Break	450	%
TD : Break	560	%
Elmendorf Tear Strength			Internal Method
MD : 44 µm	240	g
TD : 44 µm	1000	g
Film Width	185.42	cm
Yield (25.4 µm)	42.4	m²/kg

Thermal	Nominal Value	Unit
Heat Activation Temperature	96	°C

Resin Grade	Manufacturer	Category	Trademark
RheTech Polypropylene HP534-00	RheTech, Inc.	PP Copolymer	RheTech Polypropylene
SUMIPEX® MHF	Sumitomo Chemical Co., Ltd.	Acrylic (PMMA)	SUMIPEX®
NuSil MED-4720	NuSil Technology	Rubber	NuSil
INNOPOL® PP CS 2-9301	Inno-Comp Ltd.	PP Copolymer	INNOPOL® PP
Karina RED PVC COMPOUND 550D42/ 10-AT-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina