Order Products : sales@su-jiao.com
Next Nylon 6 Prime Series NGF30-01NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 6 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B4RhQe_Next-Nylon-6-Prime-Series-NGF30-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA6 Glass Fiber Reinforced FR Natural Compound Product Applications This grade is used for Electrical/Electronics Industries such as: switch parts coil former, Energy meter parts MCB Housing etc Benefits Excellent combination between Electrical and mechanical property |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.47 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.20 | -- | % | ASTM D955 |
| Transverse flow | 0.60 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.7 | -- | % | ASTM D570 |
| Saturation 1 | 5.2 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| Class m | 110 | -- | ASTM D785 | |
| Class r | 125 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 130 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | 6.0 | % | ASTM D638 |
| Flexural Modulus | 6800 | 5300 | MPa | ASTM D790 |
| Flexural Strength | 175 | 160 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 88 | 110 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 200 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 150 | -- | °C | ASTM D648 |
| Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | -- | ohms·cm | IEC 60093 |
| Dielectric Strength | 26 | 24 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | -- | UL 94 |
| Additional Information |
|---|
| 干燥 This grade is not suitable for food contact, medical devices or toy applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 240 - 250 | °C | |
| Middle Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 270 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 30T | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Axiall PVC 8903 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Delta IPP 2507 | Delta Polymers | PP Copolymer | Delta |
| Okirol® E-6 | DIOKI d.d. | PS (EPS) | Okirol® |
| EnviroTPO 2512 | West Michigan Compounding | Polyolefin, Unspecified | EnviroTPO |