Torlon® 7130
| Category: | PAI , Polyamide-imide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Torlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B3rfIk_Torlon-7130.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torlon 7130 is a 30% carbon fiber reinforced grade polyamideimide (PAI) resin. It has high strength, high modulus, excellent creep resistance, and good fatigue resistance. Thermal expansion characteristics are similar to steel, so it has excellent dimensional stability. Torlon PAI has the highest strength and rigidity among all thermoplastic resins that can withstand high temperatures of 275 ℃( 525 °F). And has excellent wear resistance, creep resistance and chemical resistance. This resin can be used for metal substitute materials, sliding blades, aviation components, impellers, shroud, pistons, housings and other components. It has injection molding and extrusion (E) grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.0 - 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.26 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 22300 | MPa | ASTM D1708 |
| -- | 16500 | MPa | ASTM D638 |
| Tensile Strength | 221 | MPa | ASTM D638 |
| Tensile Stress | 203 | MPa | ASTM D1708 |
| Tensile Elongation | |||
| Fracture 1 | 6.0 | % | ASTM D1708 |
| Fracture | 1.5 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 23°C | 19900 | MPa | ASTM D790 |
| 232°C | 15700 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| 23°C | 350 | MPa | ASTM D790 |
| 232°C | 174 | MPa | ASTM D790 |
| Compressive Modulus | 9860 | MPa | ASTM D695 |
| Compressive Strength | 254 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact | 320 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 282 | °C | ASTM D648 |
| Thermal Conductivity | 0.52 | W/m/K | ASTM C177 |
| Coefficient of Linear Thermal Expansion | 9.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 304 | °C | |
| Nozzle Temperature | 371 | °C | |
| Mold Temperature | 199 - 216 | °C | |
| Back Pressure | 6.89 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Screw L/D Ratio | 18.0:1.0 - 24.0:1.0 |
| Injection instructions |
|---|
| 最低干燥条件：350 °F （177 ° C ）温度下3小时， 300 °F （149℃ ）温度下4小时，或250 °F （121 ℃）温度下16小时。 压缩比：1：1～1.5：1 开始时，压力保持在较高的设定值6,000-8,000 psi（ 41.37-55.16MPa） ，几秒钟后，降至～3,000-5,000psi（ 20.69-34.48MPa） ，进行保压。 成型部件需进行后固化。 |
| Note Message | |
|---|---|
| 1 . | Previously, ASTM standard test method D1708 was used to measure the tensile properties of PAI and similar materials because small samples can save materials. The most widely used now is the ASTM D638 1 Bar specimen. The D1708 value contained is only used as a historical reference and is not used for comparison with the D638 value. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRAMID® 4110G35 | Samyang Corporation | Nylon, Unspecified | TRAMID® |
| Capa™ 6400 | Perstorp Holding AB | PCL | Capa™ |
| Chemical Resources RPP 5500CW | Chemical Resources, Inc. | PP Random Copolymer | Chemical Resources |
| Geon™ Vinyl Flexible R158AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LubriOne™ PC-000/5T-2S NC704 | PolyOne Corporation | PC | LubriOne™ |