PETLIN LD N125Y
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | PETLIN (MALAYSIA) SDN BHD |
| Trademark: | PETLIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | B3HR2g_PETLIN-LD-N125Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETLIN LD N125Y is a low density polyethylene resin for general purpose film applications. It is produced by the state-of-the-art DSM Stamicarbon tubular process. It contains antioxidant (BHT free), slip and antiblock additives. It is intended primarily for blown film process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | 0.10 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Film Thickness - Recommended / Available | 20 to 100 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm | 194 | MPa | |
| TD : 25 µm | 216 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 25 µm | 70.0 | MPa | |
| TD : Break, 25 µm | 25.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 25 µm | 130 | % | |
| TD : Break, 25 µm | 580 | % | |
| Dart Drop Impact (25 µm) | 77 | g | ASTM D1709 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 25 µm | 70000 | N | |
| TD : 25 µm | 25000 | N |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.0 µm) | 61 | ASTM D2457 | |
| Haze (25.0 µm) | 8.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 170 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 GB 20 FR L | RTP Company | PC | RTP |
| ARCEL® ULV (1.25 pcf) | NOVA Chemicals | PS+PE | ARCEL® |
| IROGRAN® A 70 H 4714 M | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| ISPLEN® PB 130 G1M | REPSOL | PP Impact Copolymer | ISPLEN® |
| Polycomp® PDR CB 08 | PolyPacific Pty. Ltd. | PP Copolymer | Polycomp® |